Plutonium borides
From Wikipedia, the free encyclopedia
Several plutonium borides can be formed by direct combination of plutonium and boron powders in an inert atmosphere at reduced pressure.
![Thumb image](http://upload.wikimedia.org/wikipedia/commons/thumb/d/d2/Magnesium-diboride-3D-balls.png/640px-Magnesium-diboride-3D-balls.png)
![Thumb image](http://upload.wikimedia.org/wikipedia/commons/thumb/4/44/CaHexaboride.jpg/640px-CaHexaboride.jpg)
PuB was reported to form at 1200 °C with a range of 40–70% boron. It supposedly has a Pu-B bond length of 2.46 Å and the NaCl structure, as do TiB, ZrB and HfB.[1] The existence of PuB was contested later based on several arguments.[2]
PuB2 is formed at 800 °C and has a similar structure to most other metal diborides.
At 1200 °C with 70–85% boron, mixtures of PuB4 and PuB6 are formed, with more of the latter as the temperature increases; PuB4 has the tetragonal structure (same as UB4), and PuB6 has cubic structure, same as all hexaborides (CaB6, LaB6 etc.).[1]
The most remarkable plutonium boride is arguably PuB100. Its existence[2] demonstrates the importance of contamination in boride research because as little as 1% of an impurity is capable of changing its crystal structure.