Bismuth(III) oxide

Bismuth(III) oxide is a compound of bismuth, and a common starting point for bismuth chemistry. It is found naturally as the mineral bismite (monoclinic) and sphaerobismoite (tetragonal, much more rare), but it is usually obtained as a by-product of the smelting of copper and lead ores. Dibismuth trioxide is commonly used to produce the "Dragon's eggs" effect in fireworks, as a replacement of red lead.^[1]

Bismuth(III) oxide

Names
IUPAC names Bismuth trioxide Bismuth(III) oxide Bismite (mineral)
Other names Bismuth oxide, bismuth sesquioxide
Identifiers
CAS Number	1304-76-3 Y
3D model (JSmol)	Interactive image
ChemSpider	14093 Y
ECHA InfoCard	100.013.759
EC Number	215-134-7
PubChem CID	14776
UNII	A6I4E79QF1 Y
CompTox Dashboard (EPA)	DTXSID8046537
InChI InChI=1S/2Bi.3O Y Key: WMWLMWRWZQELOS-UHFFFAOYSA-N Y InChI=1/2Bi.3O/rBi2O3/c3-1-5-2-4 Key: WMWLMWRWZQELOS-JOBWJGIYAA
SMILES O=[Bi]O[Bi]=O
Properties
Chemical formula	Bi2O3
Molar mass	465.958 g·mol−1
Appearance	yellow crystals or powder
Odor	odorless
Density	8.90 g/cm3, solid
Melting point	817 °C (1,503 °F; 1,090 K)[1]
Boiling point	1,890 °C (3,430 °F; 2,160 K)
Solubility in water	insoluble
Solubility	soluble in acids
Magnetic susceptibility (χ)	-83.0·10−6 cm3/mol
Structure
Crystal structure	monoclinic, mP20, Space group P21/c (No 14)
Coordination geometry	pseudo-octahedral
Hazards
NFPA 704 (fire diamond)	1 0 0
Flash point	Non-flammable
Safety data sheet (SDS)	ThermoFisher SDS
Related compounds
Other anions	Bismuth trisulfide Bismuth selenide Bismuth telluride
Other cations	Dinitrogen trioxide Phosphorus trioxide Arsenic trioxide Antimony trioxide
Supplementary data page
Bismuth(III) oxide (data page)
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa). Y verify (what is YN ?) Infobox references

Structure

The structures adopted by Bi₂O₃ differ substantially from those of arsenic(III) oxide, As₂O₃, and antimony(III) oxide, Sb₂O₃.^[2]

Existence domains of the four polymorphs of Bi₂O₃ as a function of temperature. (a) The α-phase transforms to the δ-phase when heated above 727 °C, which remains the structure until the melting point, 824 °C, is reached. When cooled, the δ-phase transforms into either the β-phase at 650 °C, shown in (b), or the γ-phase at 639 °C, shown in (c). The β-phase transforms to the α-phase at 303 °C. The γ-phase may persist to room temperature when the cooling rate is very slow, otherwise it transforms to the α-phase at 500 °C.^[2]

Bismuth oxide, Bi₂O₃ has five crystallographic polymorphs. The room temperature phase, α-Bi₂O₃ has a monoclinic crystal structure. There are three high temperature phases, a tetragonal β-phase, a body-centred cubic γ-phase, a cubic δ-Bi₂O₃ phase and an ε-phase. The room temperature α-phase has a complex structure with layers of oxygen atoms with layers of bismuth atoms between them. The bismuth atoms are in two different environments which can be described as distorted 6 and 5 coordinate respectively.^[3]

β-Bi₂O₃ has a structure related to fluorite.^[2]

γ-Bi₂O₃ has a structure related to that of sillenite (Bi₁₂SiO₂₀), but in which a small fraction of the bismuth atoms occupy positions occupied by silicon atoms in sillenite, so the formula may be written as Bi₁₂Bi_0.8O_19.2. The crystals are chiral (space group I23, or no. 197) with two Bi₁₂Bi_0.8O_19.2 formulas per unit cell.^[4]

δ-Bi₂O₃ has a defective fluorite-type crystal structure in which two of the eight oxygen sites in the unit cell are vacant.^[5] ε-Bi₂O₃ has a structure related to the α- and β- phases but as the structure is fully ordered it is an ionic insulator. It can be prepared by hydrothermal means and transforms to the α- phase at 400 °C.^[4]

The monoclinic α-phase transforms to the cubic δ-Bi₂O₃ when heated above 729 °C, which remains the structure until the melting point, 824 °C, is reached. The behaviour of Bi₂O₃ on cooling from the δ-phase is more complex, with the possible formation of two intermediate metastable phases; the tetragonal β-phase or the body-centred cubic γ-phase. The γ-phase can exist at room temperature with very slow cooling rates, but α-Bi₂O₃ always forms on cooling the β-phase. Even though when formed by heat, it reverts to α-Bi₂O₃ when the temperature drops back below 727 °C, δ-Bi₂O₃ can be formed directly through electrodeposition and remain relatively stable at room temperature, in an electrolyte of bismuth compounds that is also rich in sodium or potassium hydroxide so as to have a pH near 14.

Conductivity

The α-phase exhibits p-type electronic conductivity (the charge is carried by positive holes) at room temperature which transforms to n-type conductivity (charge is carried by electrons) between 550 °C and 650 °C, depending on the oxygen partial pressure. The conductivity in the β, γ and δ-phases is predominantly ionic with oxide ions being the main charge carrier. Of these δ-Bi₂O₃ has the highest reported conductivity. At 750 °C the conductivity of δ-Bi₂O₃ is typically about 1 S cm⁻¹, about three orders of magnitude greater than the intermediate phases and four orders greater than the monoclinic phase. δ-Bi₂O₃ has a defective fluorite-type crystal structure in which two of the eight oxygen sites in the unit cell are vacant. These intrinsic vacancies are highly mobile due to the high polarisability of the cation sub-lattice with the 6s² lone pair electrons of Bi³⁺. The Bi–O bonds have covalent bond character and are therefore weaker than purely ionic bonds, so the oxygen ions can jump into vacancies more freely.

The arrangement of oxygen atoms within the unit cell of δ-Bi₂O₃ has been the subject of much debate in the past. Three different models have been proposed. Sillén (1937) used powder X-ray diffraction on quenched samples and reported the structure of Bi₂O₃ was a simple cubic phase with oxygen vacancies ordered along <111>, the cube body diagonal.^[6] Gattow and Schroder (1962) rejected this model, preferring to describe each oxygen site (8c site) in the unit cell as having 75% occupancy. In other words, the six oxygen atoms are randomly distributed over the eight possible oxygen sites in the unit cell. Currently, most experts seem to favour the latter description as a completely disordered oxygen sub-lattice accounts for the high conductivity in a better way.^[7]

Willis (1965) used neutron diffraction to study the fluorite (CaF₂) system. He determined that it could not be described by the ideal fluorite crystal structure, rather, the fluorine atoms were displaced from regular 8c positions towards the centres of the interstitial positions.^[8] Shuk et al. (1996)^[9] and Sammes et al. (1999)^[10] suggest that because of the high degree of disorder in δ-Bi₂O₃, the Willis model could also be used to describe its structure.

Use in solid-oxide fuel cells (SOFCs)

Interest has centred on δ-Bi₂O₃ as it is principally an ionic conductor. In addition to electrical properties, thermal expansion properties are very important when considering possible applications for solid electrolytes. High thermal expansion coefficients represent large dimensional variations under heating and cooling, which would limit the performance of an electrolyte. The transition from the high-temperature δ-Bi₂O₃ to the intermediate β-Bi₂O₃ is accompanied by a large volume change and consequently, a deterioration of the mechanical properties of the material. This, combined with the very narrow stability range of the δ-phase (727–824 °C), has led to studies on its stabilization to room temperature.

Bi₂O₃ easily forms solid solutions with many other metal oxides. These doped systems exhibit a complex array of structures and properties dependent on the type of dopant, the dopant concentration and the thermal history of the sample. The most widely studied systems are those involving rare earth metal oxides, Ln₂O₃, including yttria, Y₂O₃. Rare earth metal cations are generally very stable, have similar chemical properties to one another and are similar in size to Bi³⁺, which has a radius of 1.03 Å, making them all excellent dopants. Furthermore, their ionic radii decrease fairly uniformly from La³⁺ (1.032 Å), through Nd³⁺ (0.983 Å), Gd³⁺ (0.938 Å), Dy³⁺ (0.912 Å) and Er³⁺ (0.89 Å), to Lu³⁺ (0.861 Å) (known as the "lanthanide contraction"), making them useful to study the effect of dopant size on the stability of the Bi₂O₃ phases.

Bi₂O₃ has also been used as sintering additive in the Sc₂O₃-doped zirconia system for intermediate temperature SOFC.^[11]

Preparation

The trioxide can be prepared by ignition of bismuth hydroxide.^[1] Bismuth trioxide can be also obtained by heating bismuth subcarbonate at approximately 400 °C.^[12]

Reactions

Atmospheric carbon dioxide or CO₂ dissolved in water readily reacts with Bi₂O₃ to generate bismuth subcarbonate.^[12] Bismuth oxide is considered a basic oxide, which explains the high reactivity with CO₂. However, when acidic cations such as Si(IV) are introduced within the structure of the bismuth oxide, the reaction with CO₂ do not occur.^[12]

Bismuth(III) oxide reacts with a mixture of concentrated aqueous sodium hydroxide and bromine or aqueous potassium hydroxide and bromine to form sodium bismuthate or potassium bismuthate, respectively.^[13]

Usage

Medical devices

Bismuth oxide is occasionally used in dental materials to make them more opaque to X-rays than the surrounding tooth structure. In particular, bismuth (III) oxide has been used in hydraulic silicate cements (HSC), originally in "MTA" (a trade name, standing for the chemically-meaningless "mineral trioxide aggregate") from 10 to 20% by mass with a mixture of mainly di- and tri-calcium silicate powders. Such HSC is used for dental treatments such as: apicoectomy, apexification, pulp capping, pulpotomy, pulp regeneration, internal repair of iatrogenic perforations, repair of resorption perforations, root canal sealing and obturation. MTA sets into a hard filling material when mixed with water. Some resin-based materials also include an HSC with bismuth oxide. Problems have allegedly arisen with bismuth oxide because it is claimed not to be inert at high pH, specifically that it slows the setting of the HSC, but also over time can lose color^[14] by exposure to light or reaction with other materials that may have been used in the tooth treatment, such as sodium hypochlorite.^[15]

Radiative cooling

Bismuth oxide was used to develop a scalable colored surface high in solar reflectance and heat emissivity for passive radiative cooling. The paint was non-toxic and demonstrated a reflectance of 99% and emittance of 97%. In field tests the coating exhibited significant cooling power and reflected potential for the further development of colored surfaces practical for large-scale radiative cooling applications.^[16]

References

1. Patnaik, Pradyot (2003). Handbook of Inorganic Chemical Compounds. McGraw-Hill. p. 243. ISBN 0-07-049439-8. Retrieved 2009-06-06.
2. Wells, A.F. (1984) Structural Inorganic Chemistry. 5th. London, England: Oxford University Press. p.890 ISBN 0-19-855370-6
3. Malmros, Gunnar; Fernholt, Liv; Ballhausen, C. J.; Ragnarsson, Ulf; Rasmussen, S. E.; Sunde, Erling; Sørensen, Nils Andreas (1970). "The Crystal Structure of alpha-Bi2O2". Acta Chemica Scandinavica. 24: 384–96. doi:10.3891/acta.chem.scand.24-0384.
4. Radaev, S. F.; Simonov, V. I.; Kargin, Yu. F. (1992). "Structural features of γ-phase Bi₂O₃ and its place in the sillenite family". Acta Crystallographica Section B. 48 (5): 604–9. doi:10.1107/S0108768192003847.
5. Harwig, H. A. (1978). "On the Structure of Bismuthsesquioxide: The α, β, γ, and δ-phase". Zeitschrift für anorganische und allgemeine Chemie. 444: 151–66. doi:10.1002/zaac.19784440118.
6. Sillén, Lars Gunnar (1937). "X-Ray Studies on Bismuth Trioxide". Arkiv för kemi, mineralogi och geologi. 12A (1). OCLC 73018207.
7. Gattow, G.; Schröder, H. (1962). "Über Wismutoxide. III. Die Kristallstruktur der Hochtemperaturmodifikation von Wismut(III)-oxid (δ-Bi2O3)" [About bismuth oxides. III. The crystal structure of the high-temperature modification of bismuth (III) oxide (δ-Bi2O3)]. Zeitschrift für anorganische und allgemeine Chemie (in German). 318 (3–4): 176–89. doi:10.1002/zaac.19623180307.
8. Willis, B. T. M. (1965). "The anomalous behaviour of the neutron reflexion of fluorite". Acta Crystallographica. 18 (1): 75–6. Bibcode:1965AcCry..18...75W. doi:10.1107/S0365110X65000130.
9. Shuk, P; Wiemhöfer, H.-D.; Guth, U.; Göpel, W.; Greenblatt, M. (1996). "Oxide ion conducting solid electrolytes based on Bi₂O₃". Solid State Ionics. 89 (3–4): 179–96. doi:10.1016/0167-2738(96)00348-7.
10. Sammes, N; Tompsett, G.A; Cai, Zhihong (1999). "The chemical reaction between ceria and fully stabilised zirconia". Solid State Ionics. 121–5 (1–4): 121–5. doi:10.1016/S0167-2738(98)00538-4.
11. Hirano, Masanori; Oda, Takayuki; Ukai, Kenji; Mizutani; Yasunobu (2003). "Effect of Bi₂O₃ additives in Sc stabilized zirconia electrolyte on a stability of crystal phase and electrolyte properties". Solid State Ionics. 158 (3–4): 215–23. doi:10.1016/S0167-2738(02)00912-8.
12. Ortiz-Quiñonez, Jose; Zumeta-Dubé, Inti; Díaz, David; Nava-Etzana, Noel; Cruz-Zaragoza, Epifanio (2017). "Bismuth Oxide Nanoparticles Partially Substituted with Eu^III, Mn^IV, and Si^IV: Structural, Spectroscopic, and Optical Findings". Inorganic Chemistry. 56 (6): 3394–3403. doi:10.1021/acs.inorgchem.6b02923. PMID 28252972. S2CID 3346966.
13. Brauer, Georg (1963), Handbook of Preparative Inorganic Chemistry, vol. 1 (2nd ed.), New York: Academic Press Inc., p. 628
14. Hutcheson, C; Seale, N. S.; McWhorter, A; Kerins, C; Wright, J (2012). "Multi-surface composite vs stainless steel crown restorations after mineral trioxide aggregate pulpotomy: A randomized controlled trial". Pediatric Dentistry. 34 (7): 460–7. PMID 23265162.
15. Camilleri, Josette (2014). "Color Stability of White Mineral Trioxide Aggregate in Contact with Hypochlorite Solution". Journal of Endodontics. 40 (3): 436–40. doi:10.1016/j.joen.2013.09.040. PMID 24565667.
16. Zhai, Huatian; Fan, Desong; Li, Qiang (September 2022). "Scalable and paint-format colored coatings for passive radiative cooling". Solar Energy Materials and Solar Cells. 245: 111853. doi:10.1016/j.solmat.2022.111853. S2CID 249877164 – via Elsevier Science Direct.

Further reading

• Shannon, R. D. (1976). "Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides". Acta Crystallographica Section A. 32 (5): 751–67. Bibcode:1976AcCrA..32..751S. doi:10.1107/S0567739476001551.
• Vannier, R.N.; Mairesse, G.; Abraham, F.; Nowogrocki, G. (1993). "Incommensurate Superlattice in Mo-Substituted Bi₄V₂O₁₁". Journal of Solid State Chemistry. 103 (2): 441–6. Bibcode:1993JSSCh.103..441V. doi:10.1006/jssc.1993.1120.