टाँका या सोल्डर (Solder) एक गलनीय मिश्रधातु है। इसका उपयोग टाँका लगाने तथा धातु के टुकड़ों को जोड़ने के काम आती है।
यह सम्पूर्ण पृष्ठ या इसके कुछ अनुभाग हिन्दी के अतिरिक्त अन्य भाषा(ओं) में भी लिखे गए हैं। आप इनका करके विकिपीडिया की सहायता कर सकते हैं। |
संरचना | गलनांक °C S/L | विषैलापन | गलनक्रांतिक | टिप्पणी | Sn | Pb | Ag | Cu | Sb | Bi | In | Zn | Cd | Au | अन्य. |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Sn50Zn49Cu1 | 200/300[1] | no | Galvanite Lead free galvanizing solder formulation designed specifically for high quality repairs to galvanized Steel surfaces. Simple, effective and easy to use, in both manufacturing and field applications. Metallurgically bonds to the Steel, for a seamless protective barrier.[1] | 50 | 1 | 49 | |||||||||
Sn90Zn7Cu3 | 200/222[2] | no | Kapp Eco-Babbitt[2] Commonly used in capacitor manufacturing as protective coating to shield against electromotive force (EMF) and electromagnetic interference (EMI) with the specified performance of the capacitor, to prevent current and charge leakage out of and within the layers of the capacitor, and to prevent the development of electron flows within the coating material itself, that would dimminish capacitor performance, coating, and capacitor life.[2] | 90 | 3 | 7 | |||||||||
Pb90Sn10 | 268/302[3] 275/302[4] | Pb | no | Sn10, UNS L54520, ASTM10B. Balls for CBGA components, replaced by Sn95.5Ag3.9Cu0.6.[5] Low cost and good bonding properties. Rapidly dissolves gold and silver, not recommended for those.[6] Used for fabrication of car radiators and fuel tanks, for coating and bonding of metals for moderate service temperatures. Body solder.[7] Has low thermal EMF, can be used as an alternative to Cd70 where parasitic thermocouple voltage has to be avoided.[8] | 10 | 90 | |||||||||
Pb88Sn12 | 254/296[7] | Pb | no | Used for fabrication of car radiators and fuel tanks, for coating and bonding of metals for moderate service temperatures. Body solder. | 12 | 88 | |||||||||
Pb85Sn15 | 227/288[7] | Pb | no | Used for coating tubes and sheets and fabrication of car radiators. Body solder. | 15 | 85 | |||||||||
Pb80Sn20 | 183/280[4] | Pb | no | Sn20, UNS L54711. Used for coating radiator tubes for joining fins.[7] | 20 | 80 | |||||||||
Pb75Sn25 | 183/266[3] | Pb | no | Crude solder for construction plumbing works, flame-melted. Used for soldering car engine radiators. Used for machine, dip and hand soldering of plumbing fixtures and fittings. Superior body solder.[7] | 25 | 75 | |||||||||
Pb70Sn30 | 185/255[3] 183/257[4] | Pb | no | Sn30, UNS L54280, crude solder for construction plumbing works, flame-melted, good for machine and torch soldering.[9] Used for soldering car engine radiators. Used for machine, dip and hand soldering of plumbing fixtures and fittings. Superior body solder.[7] | 30 | 70 | |||||||||
Pb68Sn32 | 253 | Pb | no | "Plumber solder", for construction plumbing works[10] | 32 | 68 | |||||||||
Pb68Sn30Sb2 | 185/243[4] | Pb | no | Pb68 | 30 | 68 | 2 | ||||||||
Sn30Pb50Zn20 | 177/288[11] | Pb | no | Kapp GalvRepair Economical solder for repairing & joining most metals including Aluminum and cast Iron. Have been the used for cast Iron and galvanized surface repair.[11] | 30 | 50 | 20 | ||||||||
Sn33Pb40Zn28 | 230/275[11] | Pb | no | Economical solder for repairing & joining most metals including Aluminum and cast Iron. Have been the used for cast Iron and galvanized surface repair.[11] | 33 | 40 | 28 | ||||||||
Pb67Sn33 | 187–230 | Pb | no | PM 33, crude solder for construction plumbing works, flame-melted, temperature depends on additives | 33 | 67 | |||||||||
Pb65Sn35 | 183/250[4] | Pb | no | Sn35. Used as a cheaper alternative of Sn60Pb40 for wiping and sweating joints.[7] | 35 | 65 | |||||||||
Pb60Sn40 | 183/238[3] 183/247[4] | Pb | no | Sn40, UNS L54915. For soldering of brass and car radiators.[9] For bulk soldering, and where wider melting point range is desired. For joining cables. For wiping and joining lead pipes. For repairs of radiators and electrical systems.[7] | 40 | 60 | |||||||||
Pb55Sn45 | 183/227[7] | Pb | no | For soldering radiator cores, roof seams, and for decorative joints. | 45 | 55 | |||||||||
Sn50Pb50 | 183/216[3] 183–212[4] | Pb | no | Sn50, UNS L55030. "Ordinary solder", for soldering of brass, electricity meters, gas meters, formerly also tin cans. General purpose, for standard tinning and sheetmetal work. Becomes brittle below −150 °C.[12][10] Low cost and good bonding properties. Rapidly dissolves gold and silver, not recommended for those.[6] For wiping and assembling plumbing joints for non-potable water.[7] | 50 | 50 | |||||||||
Sn50Pb48.5Cu1.5 | 183/215[13] | Pb | no | Savbit, Savbit 1, Sav1. Minimizes dissolution of copper. Originally designed to reduce erosion of the soldering iron tips. About 100 times slower erosion of copper than ordinary tin/lead alloys. Suitable for soldering thin copper platings and very thin copper wires.[14] | 50 | 48.5 | 1.5 | ||||||||
Sn60Pb40 | 183/190[3] 183/188[4] | Pb | near | Sn60, ASTM60A, ASTM60B. Common in electronics, most popular leaded alloy for dipping. Low cost and good bonding properties. Used in both SMT and through-hole electronics. Rapidly dissolves gold and silver, not recommended for those.[6] Slightly cheaper than Sn63Pb37, often used instead for cost reasons as the melting point difference is insignificant in practice. On slow cooling gives slightly duller joints than Sn63Pb37.[14] | 60 | 40 | |||||||||
Sn60Pb38Cu2 | 183/190[4][15] | Pb | Cu2. Copper content increases hardness of the alloy and inhibits dissolution of soldering iron tips and part leads in molten solder. | 60 | 38 | 2 | |||||||||
Sn60Pb39Cu1 | Pb | no | 60 | 39 | 1 | ||||||||||
Sn62Pb38 | 183 | Pb | near | "Tinman's solder", used for tinplate fabrication work.[10] | 62 | 38 | |||||||||
Sn63Pb37 | 183[16] | Pb | yes | Sn63, ASTM63A, ASTM63B. Common in electronics; exceptional tinning and wetting properties, also good for stainless steel. One of most common solders. Low cost and good bonding properties. Used in both SMT and through-hole electronics. Rapidly dissolves gold and silver, not recommended for those.[6] Sn60Pb40 is slightly cheaper and is often used instead for cost reasons, as the melting point difference is insignificant in practice. On slow cooling gives slightly brighter joints than Sn60Pb40.[14] | 63 | 37 | |||||||||
Sn63Pb37P0.0015–0.04 | 183[17] | Pb | yes | Sn63PbP. A special alloy for HASL machines. Addition of phosphorus reduces oxidation. Unsuitable for wave soldering as it may form metal foam. | 63 | 37 | P | ||||||||
Sn62Pb37Cu1 | 183[15] | Pb | yes | Similar to Sn63Pb37. Copper content increases hardness of the alloy and inhibits dissolution of soldering iron tips and part leads in molten solder. | 62 | 37 | 1 | ||||||||
Sn70Pb30 | 183/193[3] | Pb | no | Sn70 | 70 | 30 | |||||||||
Sn90Pb10 | 183/213[4] | Pb | no | formerly used for joints in food industry | 90 | 10 | |||||||||
Sn95Pb5 | 238 | Pb | no | plumbing and heating | 95 | 5 | |||||||||
Pb92Sn5.5Ag2.5 | 286/301[15] | Pb | no | For higher-temperature applications. | 5.5 | 92 | 2.5 | ||||||||
Pb80Sn12Sb8 | Pb | no | Used for soldering iron and steel[10] | 12 | 80 | 8 | |||||||||
Pb80Sn18Ag2 | 252/260[4] | Pb | no | Used for soldering iron and steel[10] | 18 | 80 | 2 | ||||||||
Pb79Sn20Sb1 | 184/270 | Pb | no | Sb1 | 20 | 79 | 1 | ||||||||
Pb55Sn43.5Sb1.5 | Pb | no | General purpose solder. Antimony content improves mechanical properties but causes brittleness when soldering cadmium, zinc, or galvanized metals.[10] | 43.5 | 55 | 1.5 | |||||||||
Sn43Pb43Bi14 | 144/163[3] | Pb | no | Bi14. Good fatigue resistance combined with low melting point. Contains phases of tin and lead-bismuth.[18] Useful for step soldering. | 43 | 43 | 14 | ||||||||
Sn46Pb46Bi8 | 120/167[4] | Pb | no | Bi8 | 46 | 46 | 8 | ||||||||
Bi52Pb32Sn16 | 96 | Pb | yes? | Bi52. Good fatigue resistance combined with low melting point. Reasonable shear strength and fatigue properties. Combination with lead-tin solder may dramatically lower melting point and lead to joint failure.[18] | 16 | 32 | 52 | ||||||||
Bi46Sn34Pb20 | 100/105[4] | Pb | no | Bi46 | 34 | 20 | 46 | ||||||||
Sn62Pb36Ag2 | 179[3] | Pb | yes | Sn62. Common in electronics. The strongest tin-lead solder. Appearance identical to Sn60Pb40 or Sn63Pb37. Crystals of Ag3Sn may be seen growing from the solder. Extended heat treatment leads to formation of crystals of binary alloys. Silver content decreases solubility of silver, making the alloy suitable for soldering silver-metallized surfaces, e.g. SMD capacitors and other silver-metallized ceramics.[12][14][18] Not recommended for gold.[6] General-purpose. | 62 | 36 | 2 | ||||||||
Sn62.5Pb36Ag2.5 | 179[3] | Pb | yes | 62.5 | 36 | 2.5 | |||||||||
Pb88Sn10Ag2 | 268/290[3] 267/299[19] | Pb | no | Sn10, Pb88. Silver content reduces solubility of silver coatings in the solder. Not recommended for gold.[6] Forms a eutectic phase, not recommended for operation above 120 °C. | 10 | 88 | 2 | ||||||||
Pb90Sn5Ag5 | 292[3] | Pb | yes | 5 | 90 | 5 | |||||||||
Pb92.5Sn5Ag2.5 | 287/296[3] 299/304[4] | Pb | no | Pb93. | 5 | 92.5 | 2.5 | ||||||||
Pb93.5Sn5Ag1.5 | 296/301[3] 305/306[4] | Pb | no | Pb94, HMP alloy, HMP. Service temperatures up to 255 °C. Useful for step soldering. Also can be used for extremely low temperatures as it remains ductile down to −200 °C, while solders with more than 20% tin become brittle below −70 °C. Higher strength and better wetting than Pb95Sn5.[14] | 5 | 93.5 | 1.5 | ||||||||
Pb95.5Sn2Ag2.5 | 299/304[3] | Pb | no | 2 | 95.5 | 2.5 | |||||||||
In97Ag3 | 143[20] | – | yes | Wettability and low-temperature malleability of indium, strength improved by addition of silver. Particularly good for cryogenic applications. Used for packaging of photonic devices. | 3 | 97 | |||||||||
In90Ag10 | 143/237[21] | – | no | Nearly as wettable and low-temperature malleable as indium. Large plastic range. Can solder silver, fired glass and ceramics. | 10 | 90 | |||||||||
In75Pb25 | 156/165[6] | Pb | no | Less gold dissolution and more ductile than lead-tin alloys. Used for die attachment, general circuit assembly and packaging closures.[6] | 25 | 75 | |||||||||
In70Pb30 | 160/174[3] 165/175[4][22] | Pb | no | In70. Suitable for gold, low gold-leaching. Good thermal fatigue properties. | 30 | 70 | |||||||||
In60Pb40 | 174/185[3] 173/181[4] | Pb | no | In60. Low gold-leaching. Good thermal fatigue properties. | 40 | 60 | |||||||||
In50Pb50 | 180/209[6] 178/210[4] | Pb | no | In50. Only one phase. Resoldering with lead-tin solder forms indium-tin and indium-lead phases and leads to formation of cracks between the phases, joint weakening and failure.[18] On gold surfaces gold-indium intermetallics tend to be formed, and the joint then fails in the gold-depleted zone and the gold-rich intermetallic.[23] Less gold dissolution and more ductile than lead-tin alloys.[6] Good thermal fatigue properties. | 50 | 50 | |||||||||
In50Sn50 | 118/125[24] | – | no | Cerroseal 35. Fairly well wets glass, quartz and many ceramics. Malleable, can compensate some thermal expansion differences. Low vapor pressure. Used in low temperature physics as a glass-wetting solder.[25] | 50 | 50 | |||||||||
In70Sn15Pb9.6Cd5.4 | 125[26] | Pb,Cd | 15 | 9.6 | 70 | 5.4 | |||||||||
Pb75In25 | 250/264[6] 240/260[27] | Pb | no | In25. Low gold-leaching. Good thermal fatigue properties. Used for die attachment of e.g. GaAs dies.[23] Used also for general circuit assembly and packaging closures. Less dissolution of gold and more ductile than tin-lead alloy.[6] | 75 | 25 | |||||||||
Sn70Pb18In12 | 162[3] 154/167[28] | Pb | yes | General purpose. Good physical properties. | 70 | 18 | 12 | ||||||||
Sn37.5Pb37.5In25 | 134/181[6] | Pb | no | Good wettability. Not recommended for gold.[6] | 37.5 | 37.5 | 25 | ||||||||
Pb90In5Ag5 | 290/310[3] | Pb | no | 90 | 5 | 5 | |||||||||
Pb92.5In5Ag2.5 | 300/310[3] | Pb | no | UNS L51510. Minimal leaching of gold, good thermal fatigue properties. Reducing atmosphere frequently used.. | 92.5 | 2.5 | 5 | ||||||||
Pb92.5In5Au2.5 | 300/310[4] | Pb | no | In5 | 92.5 | 5 | 2.5 | ||||||||
Pb94.5Ag5.5 | 305/364[4] 304/343[29] | Pb | no | Ag5.5, UNS L50180 | 94.5 | 5.5 | |||||||||
Pb95Ag5 | 305/364[30] | Pb | no | 95 | 5 | ||||||||||
Pb97.5Ag2.5 | 303[3] 304[4] 304/579[31] | Pb | yes no | Ag2.5, UNS L50132. Used during World War II to conserve tin. Poor corrosion resistance; joints suffered corrosion in both atmospheric and underground conditions, all had to be replaced with Sn-Pb alloy joints.[32] Torch solder. | 97.5 | 2.5 | |||||||||
Sn97.5Pb1Ag1.5 | 305 | Pb | yes | Important for hybrid circuits assembly.[12] | 97.5 | 1 | 1.5 | ||||||||
Pb97.5Ag1.5Sn1 | 309[3] | Pb | yes | Ag1.5, ASTM1.5S. High melting point, used for commutators, armatures, and initial solder joints where remelting when working on nearby joints is undesirable.[9] Silver content reduces solubility of silver coatings in molten solder. Not recommended for gold.[6] Standard PbAgSn eutectic solder, wide use in semiconductor assembly. Reducing protective atmosphere (e.g. 12% hydrogen) often used. High creep resistance, for use at both elevated and cryogenic temperatures. | 1 | 97.5 | 1.5 | ||||||||
Pb54Sn45Ag1 | 177–210 | Pb | exceptional strength, silver gives it a bright long-lasting finish; ideal for stainless steel[9] | 45 | 54 | 1 | |||||||||
Pb96Ag4 | 305 | Pb | high-temperature joints[9] | 96 | 4 | ||||||||||
Pb96Sn2Ag2 | 252/295[4] | Pb | Pb96 | 2 | 96 | 2 | |||||||||
Sn61Pb36Ag3 | Pb | [12] | 61 | 36 | 3 | ||||||||||
Sn56Pb39Ag5 | Pb | [12] | 56 | 39 | 5 | ||||||||||
Sn98Ag2 | – | [12] | 98 | 2 | |||||||||||
Sn65Ag25Sb10 | 233 | – | yes | Very high tensile strength. For die attachment. Very brittle. Old Motorola die attach solder. | 65 | 25 | 10 | ||||||||
Sn96.5Ag3.0Cu0.5 | 217/220 217/218[4][33] | – | near | SAC305. It is the JEITA recommended alloy for wave and reflow soldering, with alternatives SnCu for wave and SnAg and SnZnBi for reflow soldering. Usable also for selective soldering and dip soldering. At high temperatures tends to dissolve copper; copper buildup in the bath has detrimental effect (e.g. increased bridging). Copper content must be maintained between 0.4–0.85%, e.g. by refilling the bath with Sn97Ag3 alloy. Nitrogen atmosphere can be used to reduce losses by dross formation. Dull, surface shows formation of dendritic tin crystals. | 96.5 | 3 | 0.5 | ||||||||
Sn95.8Ag3.5Cu0.7 | 217–218 | – | near | SN96C-Ag3.5 A commonly used alloy. Used for wave soldering. Usable also for selective soldering and dip soldering. At high temperatures tends to dissolve copper; copper buildup in the bath has detrimental effect (e.g. increased bridging). Copper content must be maintained between 0.4–0.85%, e.g. by refilling the bath with Sn96.5Ag3.5 alloy (designated e.g. SN96Ce). Nitrogen atmosphere can be used to reduce losses by dross formation. Dull, surface shows formation of dendritic tin crystals. | 95.8 | 3.5 | 0.7 | ||||||||
Sn95.6Ag3.5Cu0.9 | 217 | – | yes | Determined by NIST to be truly eutectic. | 95.6 | 3.5 | 0.9 | ||||||||
Sn95.5Ag3.8Cu0.7 | 217[34] | – | almost | SN96C. Preferred by the European IDEALS consortium for reflow soldering. Usable also for selective soldering and dip soldering. At high temperatures tends to dissolve copper; copper buildup in the bath has detrimental effect (e.g. increased bridging). Copper content must be maintained between 0.4–0.85%, e.g. by refilling the bath with Sn96.2Ag3.8 alloy (designated e.g. SN96Ce). Nitrogen atmosphere can be used to reduce losses by dross formation. Dull, surface shows formation of dendritic tin crystals. | 95.5 | 3.8 | 0.7 | ||||||||
Sn95.25Ag3.8Cu0.7Sb0.25 | – | Preferred by the European IDEALS consortium for wave soldering. | 95.25 | 3.8 | 0.7 | 0.25 | |||||||||
Sn95.5Ag3.9Cu0.6 | 217[35] | – | yes | Recommended by the US NEMI consortium for reflow soldering. Used as balls for BGA/CSP and CBGA components, a replacement for Sn10Pb90. Solder paste for rework of BGA boards.[5] Alloy of choice for general SMT assembly. | 95.5 | 3.9 | 0.6 | ||||||||
Sn95.5Ag4Cu0.5 | 217[36] | – | yes | Lead Free, Cadmium Free formulation designed specifically to replace Lead solders in Copper and Stainless Steel plumbing, and in electrical and electronic applications.[37] | 95.5 | 4 | 0.5 | ||||||||
Sn96.5Ag3.5 | 221[3] | – | yes | Sn96, Sn96.5, 96S. Fine lamellar structure of densely distributed Ag3Sn. Annealing at 125 °C coarsens the structure and softens the solder.[5] Creeps via dislocation climb as a result of lattice diffusion.[38] Used as wire for hand soldering rework; compatible with SnCu0.7, SnAg3Cu0.5, SnAg3.9Cu0.6, and similar alloys. Used as solder spheres for BGA/CSP components. Used for step soldering and die attachment in high power devices. Established history in the industry.[5] Widely used. Strong lead-free joints. Silver content minimizes solubility of silver coatings. Not recommended for gold.[6] Marginal wetting. Good for step soldering. Used for soldering stainless steel as it wets stainless steel better than other soft solders. Silver content does not suppress dissolution of silver metallizations.[14] High tin content allows absorbing significant amount of gold without embrittlement.[39] | 96.5 | 3.5 | |||||||||
Sn96Ag4 | 221–229 | – | no | ASTM96TS. "Silver-bearing solder". Food service equipment, refrigeration, heating, air conditioning, plumbing.[9] Widely used. Strong lead-free joints. Silver content minimizes solubility of silver coatings. Not recommended for gold.[6] | 96 | 4 | |||||||||
Sn95Ag5 | 221/254[40] | – | no | Widely used. Strong lead-free joints. Silver content minimizes solubility of silver coatings. Not recommended for gold. Produces strong and ductile joints on Copper and Stainless Steel. The resulting joints have high tolerance to vibration and stress, with tensile strengths to 30,000 psi on Stainless.[40] | 95 | 5 | |||||||||
Sn94Ag6 | 221/279[40] | – | no | Produces strong and ductile joints on Copper and Stainless Steel. The resulting joints have high tolerance to vibration and stress, with tensile strengths to 30,000 psi on Stainless.[40] | 94 | 6 | |||||||||
Sn93Ag7 | 221/302[40] | – | no | Produces strong and ductile joints on Copper and Stainless Steel. The resulting joints have high tolerance to vibration and stress, with tensile strengths to 31,000 psi on Stainless.[40] Audio industry standard for vehicle and home theater speaker installations. Its 7% Silver content requires a higher temperature range, but yields superior strength and vibration resistance.[41] | 93 | 7 | |||||||||
Sn95Ag4Cu1 | – | 95 | 4 | 1 | |||||||||||
Sn | 232 | – | pure | Sn99. Good strength, non-dulling. Use in food processing equipment, wire tinning, and alloying.[9] Susceptible to tin pest. | 99.99 | ||||||||||
Sn99.3Cu0.7 | 227 | – | yes | Sn99Cu1. Also designated as Sn99Cu1. Cheap alternative for wave soldering, recommended by the US NEMI consortium. Coarse microstructure with ductile fractures. Sparsely distributed Cu6Sn5.[42] Forms large dendritic ß-tin crystals in a network of eutectic microstructure with finely dispersed Cu6Sn5. High melting point unfavorable for SMT use. Low strength, high ductility. Susceptible to tin pest.[38] Addition of small amount of nickel increases its fluidity; the highest increase occurs at 0.06% Ni. Such alloys are known as nickel modified or nickel stabilized.[43] | 99.3 | 0.7 | (Ni) | ||||||||
Sn99Cu0.7Ag0.3 | 217/228[44] | – | no | SCA, SAC, or SnAgCu. Tin-silver-copper alloy. Relatively low-cost lead-free alloy for simple applications. Can be used for wave, selective and dip soldering. At high temperatures tends to dissolve copper; copper buildup in the bath has detrimental effect (e.g. increased bridging). Copper content must be maintained between 0.4–0.85%, e.g. by refilling the bath with Sn96.2Ag3.8 alloy (designated e.g. SN96Ce). Nitrogen atmosphere can be used to reduce losses by dross formation. Dull, surface shows formation of dendritic tin crystals. | 99 | 0.3 | 0.7 | ||||||||
Sn97Cu3 | 227/250[45] 232/332[7] | – | For high-temperature uses. Allows removing insulation from an enameled wire and applying solder coating in a single operation. For radiator repairs, stained glass windows, and potable water plumbing. | 97 | 3 | ||||||||||
Sn97Cu2.75Ag0.25 | 228/314[7] | – | High hardness, creep-resistant. For radiators, stained glass windows, and potable water plumbing. Excellent high-strength solder for radiator repairs. Wide range of patina and colors. | 97 | 0.25 | 2.75 | |||||||||
Zn100 | 419 | – | pure | For soldering aluminium. Good wettability of aluminium, relatively good corrosion resistance.[46] | 100 | ||||||||||
Bi100 | 271 | – | pure | Used as a non-superconducting solder in low-temperature physics. Does not wet metals well, forms a mechanically weak joint.[25] | 100 | ||||||||||
Sn91Zn9 | 199[47] | – | yes | KappAloy9 Designed specifically for Aluminum-to-Aluminum and Aluminum-to-Copper soldering. It has good corrosion resistance and tensile strength. Lies between soft solder and silver brazing alloys, thereby avoiding damage to critical electronics and substrate deformation and segregation. Best solder for Aluminum wire to Copper busses or Copper wire to Aluminum busses or contacts.[47] UNS#: L91090 | 91 | 9 | |||||||||
Sn85Zn15 | 199/260[47] | – | no | KappAloy15 Designed specifically for Aluminum-to-Aluminum and Aluminum-to-Copper soldering. It has good corrosion resistance and tensile strength. Lies between soft solder and silver brazing alloys, thereby avoiding damage to critical electronics and substrate deformation and segregation. Has a wide plastic range this makes it ideal for hand soldering Aluminum plates and parts, allowing manipulation of the parts as the solder cools.[47] | 85 | 15 | |||||||||
Zn95Al5 | 382 | – | yes | For soldering aluminium. Good wetting.[46] | 95 | Al5 | |||||||||
Sn91.8Bi4.8Ag3.4 | 211/213[48] | – | no | Do not use on lead-containing metallizations. U.S. Patent 5,439,639 (ICA Licensed Sandia Patent). | 91.8 | 3.4 | 4.8 | ||||||||
Sn70Zn30 | 199/316[47] | – | no | KappAloy30 For soldering of aluminium. Good wetting. Used extensively in spray wire form for capacitors and other electronic parts. Higher temperature and higher tensile strength compared to 85Sn/15Zn and 91Sn/9Zn.[47] | 70 | 30 | |||||||||
Sn80Zn20 | 199/288[47] | – | no | KappAloy20 For soldering of aluminium. Good wetting. Used extensively in spray wire form for capacitors and other electronic parts. Higher temperature and higher tensile strength compared to 85Sn/15Zn and 91Sn/9Zn.[47] | 80 | 20 | |||||||||
Sn60Zn40 | 199/343[47] | – | no | KappAloy40 For soldering of aluminium. Good wetting. Used extensively in spray wire form for capacitors and other electronic parts. Higher temperature and higher tensile strength compared to 85Sn/15Zn and 91Sn/9Zn.[47] | 60 | 40 | |||||||||
Pb63Sn35Sb2 | 185/243[4] | Pb | no | Sb2 | 35 | 63 | 2 | ||||||||
Pb63Sn34Zn3 | 170/256 | Pb | no | Poor wetting of aluminium. Poor corrosion rating.[32] | 34 | 63 | 3 | ||||||||
Pb92Cd8 | 310? | Pb,Cd | ? | For soldering aluminium. US patent 1,333,666.[49] | 92 | 8 | |||||||||
Sn48Bi32Pb20 | 140/160[15] | Pb | no | For low-temperature soldering of heat-sensitive parts, and for soldering in the vicinity of already soldered joints without their remelting. | 48 | 20 | 32 | ||||||||
Sn89Zn8Bi3 | 191–198 | – | Prone to corrosion and oxidation due to its zinc content. On copper surfaces forms a brittle Cu-Zn intermetallic layer, reducing the fatigue resistance of the joint; nickel plating of copper inhibits this.[50] | 89 | 3 | 8 | |||||||||
Sn83.6Zn7.6In8.8 | 181/187[51] | – | no | High dross due to zinc. Covered by U.S. Patent #5,242,658. | 83.6 | 8.8 | 7.6 | ||||||||
Sn86.5Zn5.5In4.5Bi3.5 | 174/186[52] | – | no | Lead-free. Corrosion concerns and high drossing due to zinc content. | 86.5 | 3.5 | 4.5 | 5.5 | |||||||
Sn86.9In10Ag3.1 | 204/205[53] | – | Potential use in flip-chip assembly, no issues with tin-indium eutectic phase. | 86.9 | 3.1 | 10 | |||||||||
Sn95Ag3.5Zn1Cu0.5 | 221L[50] | – | no | 95 | 3.5 | 0.5 | 1 | ||||||||
Sn95Sb5 | 235/240[3] 232/240[4] | – | no | Sb5, ASTM95TA. The US plumbing industry standard. It displays good resistance to thermal fatigue and good shear strength. Forms coarse dendrites of tin-rich solid solution with SbSn intermetallic dispersed between. Very high room-temperature ductility. Creeps via viscous glide of dislocations by pipe diffusion. More creep-resistant than SnAg3.5. Antimony can be toxic. Used for sealing chip packagings, attaching I/O pins to ceramic substrates, and die attachment; a possible lower-temperature replacement of AuSn.[38] High strength and bright finish. Use in air conditioning, refrigeration, some food containers, and high-temperature applications.[9] Good wettability, good long-term shear strength at 100 °C. Suitable for potable water systems. Used for stained glass, plumbing, and radiator repairs. | 95 | 5 | |||||||||
Sn97Sb3 | 232/238[54] | – | no | 97 | 3 | ||||||||||
Sn99Sb1 | 232/235[55] | – | no | 99 | 1 | ||||||||||
Sn99Ag0.3Cu0.7 | – | 99 | 0.3 | 0.7 | |||||||||||
Sn96.2Ag2.5Cu0.8Sb0.5 | 217–225 217[4] | – | Ag03A. Patented by AIM alliance. | 96.2 | 2.5 | 0.8 | 0.5 | ||||||||
Sn88In8.0Ag3.5Bi0.5 | 197–208 | – | Patented by Matsushita/Panasonic. | 88 | 3.5 | 0.5 | 8 | ||||||||
Bi57Sn42Ag1 | 137/139 139/140[56] | – | Addition of silver improves mechanical strength. Established history of use. Good thermal fatigue performance. Patented by Motorola. | 42 | 1 | 57 | |||||||||
Bi58Sn42 | 138[3][6] | – | yes | Bi58. Reasonable shear strength and fatigue properties. Combination with lead-tin solder may dramatically lower melting point and lead to joint failure.[18] Low-temperature eutectic solder with high strength.[6] Particularly strong, very brittle.[3] Used extensively in through-hole technology assemblies in IBM mainframe computers where low soldering temperature was required. Can be used as a coating of copper particles to facilitate their bonding under pressure/heat and creating a conductive metallurgical joint.[50] Sensitive to shear rate. Good for electronics. Used in thermoelectric applications. Good thermal fatigue performance.[57] Established history of use. Expands slightly on casting, then undergoes very low further shrinkage or expansion, unlike many other low-temperature alloys which continue changing dimensions for some hours after solidification.[25] | 42 | 58 | |||||||||
Bi58Pb42 | 124/126[58] | Pb | 42 | 58 | |||||||||||
In80Pb15Ag5 | 142/149[4] 149/154[59] | Pb | no | In80. Compatible with gold, minimum gold-leaching. Resistant to thermal fatigue. Can be used in step soldering. | 15 | 5 | 80 | ||||||||
Pb60In40 | 195/225[4] | Pb | no | In40. Low gold-leaching. Good thermal fatigue properties. | 60 | 40 | |||||||||
Pb70In30 | 245/260[4] | Pb | no | In30 | 70 | 30 | |||||||||
Sn37.5Pb37.5In26 | 134/181[4] | Pb | no | In26 | 37.5 | 37.5 | 26 | ||||||||
Sn54Pb26In20 | 130/154[4] 140/152[60] | Pb | no | In20 | 54 | 26 | 20 | ||||||||
Pb81In19 | 270/280[4] 260/275[61] | Pb | no | In19. Low gold-leaching. Good thermal fatigue properties. | 81 | 19 | |||||||||
In52Sn48 | 118 | – | yes | In52. Suitable for the cases where low-temperature soldering is needed. Can be used for glass sealing.[50] Sharp melting point. Good wettability of glass, quartz, and many ceramics. Good low-temperature malleability, can compensate for different thermal expansion coefficients of joined materials. | 48 | 52 | |||||||||
Sn52In48 | 118/131[3] | – | no | very low tensile strength | 52 | 48 | |||||||||
Sn58In42 | 118/145[62] | – | no | 58 | 42 | ||||||||||
Sn51.2Pb30.6Cd18.2 | 145[63] | Pb,Cd | yes | General-purpose. Maintains creep strength well. Unsuitable for gold. | 51.2 | 30.6 | 18.2 | ||||||||
Sn77.2In20Ag2.8 | 175/187[64] | – | no | Similar mechanical properties with Sn63Pb37, Sn62Pb36Ag2 and Sn60Pb40, suitable lead-free replacement. Contains eutectic Sn-In phase with melting point at 118 °C, avoid use above 100 °C. | 77.2 | 2.8 | 20 | ||||||||
In74Cd26 | 123[65] | Cd | yes | 74 | 26 | ||||||||||
In61.7Bi30.8Cd7.5 | 62[66] | Cd | yes | 30.8 | 61.7 | 7.5 | |||||||||
Bi47.5Pb25.4Sn12.6Cd9.5In5 | 57/65[67] | Pb,Cd | no | 12.6 | 25.4 | 47.5 | 5 | 9.5 | |||||||
Bi48Pb25.4Sn12.8Cd9.6In4 | 61/65[68] | Pb,Cd | no | 12.8 | 25.4 | 48 | 9.6 | ||||||||
Bi49Pb18Sn15In18 | 58/69[69] | Pb | no | 15 | 18 | 49 | 18 | ||||||||
Bi49Pb18Sn12In21 | 58 | Pb | yes | Cerrolow 136. Slightly expands on cooling, later shows slight shrinkage in couple hours afterwards. Used as a solder in low-temperature physics.[25] | 12 | 18 | 49 | 21 | |||||||
Bi50.5Pb27.8Sn12.4Cd9.3 | 70/73[70] | Pb,Cd | no | 12.4 | 27.8 | 50.5 | 9.3 | ||||||||
Bi50Pb26.7Sn13.3Cd10 | 70 | Pb,Cd | yes | Cerrobend. Used in low-temperature physics as a solder.[25] | 13.3 | 26.7 | 50 | 10 | |||||||
Bi44.7Pb22.6In19.1Cd5.3Sn8.3 | 47 | Cd,Pb | yes | Cerrolow 117. Used as a solder in low-temperature physics.[25] | 8.3 | 22.6 | 44.7 | 19.1 | 5.3 | ||||||
In60Sn40 | 113/122[3] | – | no | 40 | 60 | ||||||||||
In51.0Bi32.5Sn16.5 | 60.5 | – | yes | Field's metal | 16.5 | 32.5 | 51 | ||||||||
Bi49.5Pb27.3Sn13.1Cd10.1 | 70.9 | Pb,Cd | yes | Lipowitz Metal | 13.1 | 27.3 | 49.5 | 10.1 | |||||||
Bi50.0Pb25.0Sn12.5Cd12.5 | 71 | Pb,Cd | yes | Wood's metal, mostly used for casting. | 12.5 | 25 | 50 | 12.5 | |||||||
Bi50.0Pb31.2Sn18.8 | 97 | Pb | no | Newton's metal | 18.8 | 31.2 | 50 | ||||||||
Bi50Pb28Sn22 | 109 | Pb | no | Rose's metal. It was used to secure cast iron railings and balusters in pockets in stone bases and steps. Does not contract on cooling. | 22 | 28 | 50 | ||||||||
Cd95Ag5 | 338/393[71] | Cd | no | KappTec General purpose solder that will join all solderable metals except Aluminum. High temperature, high strength solder. It is used in applications where alloys melting higher than soft solders are required, but the cost and strength of Silver-brazing alloys is not necessary.[71] | 5 | 95 | |||||||||
Cd82.5Zn17.5 | 265[72] | Cd | yes | Medium temperature alloy that provide strong, corrosion-resistant joints on most metals.[72] Also for soldering aluminium and die-cast zinc alloys.[10] Used in cryogenic physics for ataching electrical potential leads to specimens of metals, as this alloy does not become superconductive at liquid helium temperatures.[25] | 17.5 | 82.5 | |||||||||
Cd70Zn30 | 265/300[72] | Cd | no | Medium temperature alloy that provide strong, corrosion-resistant joints on most metals. Works especially well on Aluminum-to-Aluminum and Aluminum-to-Copper joints, with excellent corrosion resistance and superior strength in high vibration and high stress applications in electronics, lighting and electrical products.[72] | 30 | 70 | |||||||||
Cd60Zn40 | 265/316[72] | Cd | no | Medium temperature alloy that provide strong, corrosion-resistant joints on most metals. Works especially well on Aluminum-to-Aluminum and Aluminum-to-Copper joints, with excellent corrosion resistance and superior strength in high vibration and high stress applications in electronics, lighting and electrical products.[72] | 40 | 60 | |||||||||
Cd78Zn17Ag5 | 249/316[73] | Cd | no | KappTecZ High temperature, high strength solder that may be used on most metals, but works extremely well on Aluminum, Copper and Stainless Steel. It has a high tolerance to vibration and stress, and good elongation for use on dissimilar metals. Above its liquidus of 600°F, this solder is extremely fluid and will penetrate the closest joints.[73] | 5 | 17 | 78 | ||||||||
Sn40Zn27Cd33 | 176/260[74] | Cd | no | KappRad[74] Developed specifically to join and repair Aluminum and Aluminum/Copper radiators and heat exchangers. A lower melting point makes delicate repair work easier.[74] | 40 | 27 | 33 | ||||||||
Zn90Cd10 | 265/399 | Cd | For soldering aluminium. Good wetting.[46] | 90 | 10 | ||||||||||
Zn60Cd40 | 265/335 | Cd | For soldering aluminium. Very good wetting.[46] | 60 | 40 | ||||||||||
Cd70Sn30 | 140/160[4] | Cd | no | Cd70, thermal-free solder. Produces low thermal EMF joints in copper, does not form parasitic thermocouples. Used in low-temperature physics.[25] | 29.56 | 70.44 | |||||||||
Sn50Pb32Cd18 | 145[4] | Cd,Pb | Cd18 | 50 | 32 | 18 | |||||||||
Sn40Pb42Cd18 | 145[75] | Cd,Pb | Low melting temperature allows repairing pewter and zinc objects, including die-cast toys. | 40 | 42 | 18 | |||||||||
Zn70Sn30 | 199/376 | – | no | For soldering aluminium. Excellent wetting.[32] Good strength. | 30 | 70 | |||||||||
Zn60Sn40 | 199/341 | – | no | For soldering aluminium. Good wetting.[46] | 40 | 60 | |||||||||
Zn95Sn5 | 382 | – | yes? | For soldering aluminium. Excellent wetting.[32] | 5 | 95 | |||||||||
Sn90Au10 | 217[76] | – | yes | 90 | 10 | ||||||||||
Au80Sn20 | 280 | – | yes | Au80. Good wetting, high strength, low creep, high corrosion resistance, high thermal conductivity, high surface tension, zero wetting angle. Suitable for step soldering. The original flux-less alloy, does not need flux. Used for die attachment and attachment of metal lids to semiconductor packages, e.g. kovar lids to ceramic chip carriers. Coefficient of expansion matching many common materials. Due to zero wetting angle requires pressure to form a void-free joint. Alloy of choice for joining gold-plated and gold-alloy plated surfaces. As some gold dissolves from the surfaces during soldering and moves the composition to non-eutectic state (1% increase of Au content can increase melting point by 30 °C), subsequent desoldering requires higher temperature.[77] Forms a mixture of two brittle intermetallic phases, AuSn and Au5Sn.[78] Brittle. Proper wetting achieved usually by using nickel surfaces with gold layer on top on both sides of the joint. Comprehensively tested through military standard environmental conditioning. Good long-term electrical performance, history of reliability.[23] Low vapor pressure, suitable for vacuum work. Generally used in applications that require a melting temperature over 150°C.[79] Good ductility. Also classified as a braze. | 20 | 80 | |||||||||
Au98Si2 | 370/800[4] | – | Au98. A non-eutectic alloy used for die attachment of silicon dies. Ultrasonic assistance is needed to scrub the chip surface so a eutectic (3.1% Si) is reached at reflow. | 98 | Si2 | ||||||||||
Au96.8Si3.2 | 370[4] 363[80] | – | yes | Au97.[77] AuSi3.2 is a eutectic with melting point of 363 °C. AuSi forms a meniscus at the edge of the chip, unlike AuSn, as AuSi reacts with the chip surface. Forms a composite material structure of submicron silicon plates in soft gold matrix. Tough, slow crack propagation.[42] | 96.8 | Si3.2 | |||||||||
Au87.5Ge12.5 | 361 356[4] | – | yes | Au88. Used for die attachment of some chips.[3] The high temperature may be detrimental to the chips and limits reworkability.[23] | 87.5 | Ge12.5 | |||||||||
Au82In18 | 451/485[4] | – | no | Au82. High-temperature, extremely hard, very stiff. | 18 | 82 | |||||||||
In100 | 157 | – | pure | In99. Used for die attachment of some chips. More suitable for soldering gold, dissolution rate of gold is 17 times slower than in tin-based solders and up to 20% of gold can be tolerated without significant embrittlement. Good performance at cryogenic temperatures.[81] Wets many surfaces incl. quartz, glass, and many ceramics. Deforms indefinitely under load. Does not become brittle even at low temperatures. Used as a solder in low-temperature physics, will bond to aluminium. Can be used for soldering to thin metal films or glass with an ultrasonic soldering iron.[25] | 99.99 |
Seamless Wikipedia browsing. On steroids.
Every time you click a link to Wikipedia, Wiktionary or Wikiquote in your browser's search results, it will show the modern Wikiwand interface.
Wikiwand extension is a five stars, simple, with minimum permission required to keep your browsing private, safe and transparent.