Residual-resistance ratio

Residual-resistivity ratio (also known as Residual-resistance ratio or just RRR) is usually defined as the ratio of the resistivity of a material at room temperature and at 0 K. Of course, 0 K can never be reached in practice so some estimation is usually made. Since the RRR can vary quite strongly for a single material depending on the amount of impurities and other crystallographic defects, it serves as a rough index of the purity and overall quality of a sample. Since resistivity usually increases as defect prevalence increases, a large RRR is associated with a pure sample. RRR is also important for characterizing certain unusual low temperature states such as the Kondo effect and superconductivity. Note that since it is a unitless ratio there is no difference between a residual resistivity and residual-resistance ratio.

Background

Usually at "warm" temperatures the resistivity of a metal varies linearly with temperature. That is, a plot of the resistivity as a function of temperature is a straight line. If this straight line were extrapolated all the way down to absolute zero, a theoretical RRR could be calculated

${\displaystyle RRR={\rho _{300K} \over \rho _{0K}}}$

In the simplest case of a good metal that is free of scattering mechanisms one would expect ρ_(0K) = 0, which would cause RRR to diverge. However, usually this is not the case because defects such as grain boundaries, impurities, etc. act as scattering sources that contribute a temperature independent ρ₀ value. This shifts the intercept of the curve to a higher number, giving a smaller RRR.

In practice the resistivity of a given sample is measured down to as cold as possible, which on typical laboratory instruments is in the range of 2 K, though much lower is possible. By this point the linear resistive behavior is usually no longer applicable and by the low temperature ρ is taken as a good approximation to 0 K.

Special Cases

• For superconducting materials, RRR is calculated differently because ρ is always exactly 0 below the critical temperature, T_c, which may be significantly above 0 K. In this case the RRR is calculated using the ρ from just above the superconducting transition temperature instead of at 0 K. For example, superconducting Niobium–titanium wires have an RRR defined as ${\displaystyle \rho (293K)/\rho (10K)}$.^[1]
• In the Kondo effect the resistivity begins to increase again with cooling at very low temperatures, and the value of RRR is useful for characterizing this state.

Examples

• The RRR of copper wire is generally ~ 40–50 when used for telephone lines, etc.

References

1. Z. Charifoulline (June 2006). "Residual Resistivity Ratio (RRR) Measurements of LHC Superconducting NbTi Cable Strands". IEEE Transactions on Applied Superconductivity. 16 (2): 1188–1191. Bibcode:2006ITAS...16.1188C. doi:10.1109/TASC.2006.873322. S2CID 38953248.

Bibliography

• Ashcroft, Neil W.; Mermin, N. David (1976). Solid State Physics. Holt, Rinehart and Winston. ISBN 0-03-083993-9.